HTC500 Aerogel Coating

Specification

Nano-aerogel composite thermal insulation Coating is a new type of thermal insulation material. It is a viscous slurry made of a variety of inorganic fibers, nano-silica aerogel fillers, and other materials, using water as a dispersion medium, adding a special binder, and fiber dissolution and stirring. It can be directly coated on the substrate of the protected metal or other materials by spraying or daubing, etc., Forming a protective layer with high-efficiency heat preservation by baking and curing at room temperature or low temperature.

The product has the characteristics of low thermal conductivity, high bonding strength, short drying time, low shrinkage, and is not easy to crack after drying. It's the best choice for equipment, storage tanks, special shapes, and complex working conditions.

Item Unit Technical Data
Temperature Max. ºC 500
Slurry Density kg/m³ 850
pH 8.5
Dry density kg/m³ 260
Volume shrinkage % ≤5
Tensile Strength (After Dry) kPa 476
Bond strength kPa 86
Thermal Conductivity(25ºC) W/(m·K) 0.05
Hydrophobic rate % 97.6
Non-combustibility A1 Grade
10mm thickness/m2 material kg 11
Bucket loading quantity kg 20
Application advantages of HTC500 Aerogel Coating

1. Superior Insulation Performance : 2~5 times better than traditional insulation products with longer service life
2. Reduced Insulation Thickness : For the same insulation performance, just take a portion of the thickness of traditional material
3. Hydrophobicity and Fire-proof : Repel water from penetrating into pipes, equipment, A1 rating of fire-proof
4. Easy Handling : Lightweight, easily cut and sewn to fit different shapes of pipes and equipment, Less labor for installation
5. Transportation Costs Savings : Lower packing volume and lower weight can greatly cut down logistics costs